CARBON |
|||||
PROPERTIES |
UNI
T |
BAKELITE |
RESIN |
FURANE |
PTFE |
Density |
g/cm |
18.5 |
1.75 |
1.9 |
1.9 |
| Strength |
mpa |
50 |
50 |
50 |
50 |
|---|---|---|---|---|---|
Compressive Strg |
mpa |
150 |
120 |
130 |
170 |
| Hardness |
gpa |
70 |
75 |
60 |
100 |
Porosity |
% |
2.5 |
2 |
3 |
5 |
| Feature |
Resistant against acid, working temp -100 ~
170 C |
Resistant against alkali, working temp -100
~ 200C |
Resistant against acid, alkali, working temp.
- 100 ~ 200 C |
Resistant against acid, alkali, working temp.
-100 ~ 200C |
|
SILICON
CARBIDE |
|||
PROPERTIES |
UNIT |
J(REACTION) |
S(SINTERED) |
| Purity |
% |
>90 |
>99.4 |
|---|---|---|---|
Density |
g/cm |
3.1 |
3 |
| Porosity |
% |
<3 |
0 |
Compressive Strength |
mpa |
2500 |
1000 |
| Bending Strength @ 20 C |
mpa |
>400 |
>250 |
mpa |
>400 |
>250 |
|
| Young Modules |
gpa |
400 |
330 |
TUNGSTEN
CARBIDE |
|||
PROPERTIES |
UNIT |
NICKLE |
COBOLT |
Density |
g/cm |
14.6 |
15 |
| Porosity |
% |
0 |
0 |
|---|---|---|---|
Compressive Strength |
mpa |
5000 |
5000 |
| Bending Strength |
mpa |
1600 |
1600 |
Young Modules |
gpa |
600 |
600 |
| Working Temperature |
C |
800 |
800 |
Hardness |
gpa |
13.4 |
15 |